Details structure:
- No. 02 supports consisting of No. 03 silhouettes in galvanized sheet thickness 40/10 each with decorative empty square in shape ;
- No. 04 seat made with planks of pine wood .
Metal structure :
Pre- treatment :
- Before painting , the product is pre-treated with a special cleaning spray with liquid degreasers. Then it is dried in a dryer for 15 min .
Anti-corrosion treatment :
- The article is subjected to a first coating cycle using an anticorrosive primer in thermosetting powder based on epoxy resins with special pigments to protect it from atmospheric agents .
Before cooking (corrosion ) :
- Is subsequently subjected to a first baking period of 15 min at a temperature of 180 ° . In this phase the anticorrosive polymerizes , forming a coating thickness of about 60 microns .
Painting: The product is subjected to a final cycle of thermosetting powder coating with polyester resin color " bright aluminum ." The coating is performed with electrostatic spray equipment that allows the dust to settle evenly on the pieces , forming a minimum thickness of 60 microns.
Glaze firing :
- The coated article is subjected to a final baking in the oven for a period of 20 min at a temperature of 160 ° .
Fixing:
- The supports are fitted with perforated plates for anchoring to the ground by means of anchor bolts to screw anchors ;
- The bench is provided with assembly kit , stainless steel hardware and mounting instructions .
Planks Impregnated high-pressure autoclave with concentrated saline fluid . This treatment gives the planks a preventative prevention against attack by fungi and insects .
Size:
Seat height 47.5 cm ;
Seat width 40 cm ;
Overall height 40 cm at the base ;
Lunghezzo 190 cm
Weight 40 Kg